EN 1.8838 Steel vs. S32003 Stainless Steel

Both EN 1.8838 steel and S32003 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.8838 steel and the bottom bar is S32003 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
250
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
28
Fatigue Strength, MPa 290
370
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
79
Shear Strength, MPa 380
480
Tensile Strength: Ultimate (UTS), MPa 610
730
Tensile Strength: Yield (Proof), MPa 430
510

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 410
1010
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 44
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
14
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
3.0
Embodied Energy, MJ/kg 23
42
Embodied Water, L/kg 50
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
180
Resilience: Unit (Modulus of Resilience), kJ/m3 500
660
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
26
Strength to Weight: Bending, points 20
23
Thermal Diffusivity, mm2/s 12
4.0
Thermal Shock Resistance, points 18
21

Alloy Composition

Aluminum (Al), % 0.015 to 0.054
0
Carbon (C), % 0 to 0.18
0 to 0.030
Chromium (Cr), % 0 to 0.35
19.5 to 22.5
Copper (Cu), % 0 to 0.6
0
Iron (Fe), % 95 to 99.985
68.2 to 75.9
Manganese (Mn), % 0 to 1.8
0 to 2.0
Molybdenum (Mo), % 0 to 0.23
1.5 to 2.0
Nickel (Ni), % 0 to 0.85
3.0 to 4.0
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.027
0.14 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.65
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.020
Titanium (Ti), % 0 to 0.060
0
Vanadium (V), % 0 to 0.14