EN 1.8865 Steel vs. EN 1.0303 Steel

Both EN 1.8865 steel and EN 1.0303 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.8865 steel and the bottom bar is EN 1.0303 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
84 to 120
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
12 to 25
Fatigue Strength, MPa 340
150 to 230
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 410
220 to 260
Tensile Strength: Ultimate (UTS), MPa 660
290 to 410
Tensile Strength: Yield (Proof), MPa 500
200 to 320

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 3.2
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.8
1.4
Embodied Energy, MJ/kg 24
18
Embodied Water, L/kg 52
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
30 to 94
Resilience: Unit (Modulus of Resilience), kJ/m3 670
110 to 270
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
10 to 15
Strength to Weight: Bending, points 21
12 to 16
Thermal Diffusivity, mm2/s 10
14
Thermal Shock Resistance, points 19
9.2 to 13

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Boron (B), % 0 to 0.0050
0
Carbon (C), % 0 to 0.18
0.020 to 0.060
Chromium (Cr), % 0 to 1.0
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 93.6 to 100
99.335 to 99.71
Manganese (Mn), % 0 to 1.7
0.25 to 0.4
Molybdenum (Mo), % 0 to 0.7
0
Nickel (Ni), % 0 to 1.5
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.020
0 to 0.020
Silicon (Si), % 0 to 0.6
0 to 0.1
Sulfur (S), % 0 to 0.0050
0 to 0.025
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.080
0
Zirconium (Zr), % 0 to 0.15
0