EN 1.8865 Steel vs. EN 1.1133 Steel

Both EN 1.8865 steel and EN 1.1133 steel are iron alloys. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.8865 steel and the bottom bar is EN 1.1133 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
170 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
19 to 24
Fatigue Strength, MPa 340
230 to 310
Impact Strength: V-Notched Charpy, J 110
45 to 48
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 410
370 to 380
Tensile Strength: Ultimate (UTS), MPa 660
580 to 620
Tensile Strength: Yield (Proof), MPa 500
320 to 460

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
49
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 3.2
2.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.5
Embodied Energy, MJ/kg 24
19
Embodied Water, L/kg 52
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 670
270 to 550
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
21 to 22
Strength to Weight: Bending, points 21
20 to 21
Thermal Diffusivity, mm2/s 10
13
Thermal Shock Resistance, points 19
18 to 19

Alloy Composition

Boron (B), % 0 to 0.0050
0
Carbon (C), % 0 to 0.18
0.17 to 0.23
Chromium (Cr), % 0 to 1.0
0 to 0.4
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 93.6 to 100
96.9 to 98.8
Manganese (Mn), % 0 to 1.7
1.0 to 1.5
Molybdenum (Mo), % 0 to 0.7
0 to 0.1
Nickel (Ni), % 0 to 1.5
0 to 0.4
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.6
0 to 0.4
Sulfur (S), % 0 to 0.0050
0 to 0.035
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.080
0
Zirconium (Zr), % 0 to 0.15
0