EN 1.8865 Steel vs. S42035 Stainless Steel

Both EN 1.8865 steel and S42035 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.8865 steel and the bottom bar is S42035 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
160
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
18
Fatigue Strength, MPa 340
260
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 410
390
Tensile Strength: Ultimate (UTS), MPa 660
630
Tensile Strength: Yield (Proof), MPa 500
430

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 420
810
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
27
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 3.2
9.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.8
2.4
Embodied Energy, MJ/kg 24
34
Embodied Water, L/kg 52
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
100
Resilience: Unit (Modulus of Resilience), kJ/m3 670
460
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
22
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 10
7.2
Thermal Shock Resistance, points 19
22

Alloy Composition

Boron (B), % 0 to 0.0050
0
Carbon (C), % 0 to 0.18
0 to 0.080
Chromium (Cr), % 0 to 1.0
13.5 to 15.5
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 93.6 to 100
78.1 to 85
Manganese (Mn), % 0 to 1.7
0 to 1.0
Molybdenum (Mo), % 0 to 0.7
0.2 to 1.2
Nickel (Ni), % 0 to 1.5
1.0 to 2.5
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.0050
0 to 0.030
Titanium (Ti), % 0 to 0.050
0.3 to 0.5
Vanadium (V), % 0 to 0.080
0
Zirconium (Zr), % 0 to 0.15
0