EN 1.8874 Steel vs. AWS E316

Both EN 1.8874 steel and AWS E316 are iron alloys. They have 67% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.8874 steel and the bottom bar is AWS E316.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
34
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 660
580

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
15
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 3.2
20
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.8
4.0
Embodied Energy, MJ/kg 24
55
Embodied Water, L/kg 52
160

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
20
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 10
4.0
Thermal Shock Resistance, points 19
15

Alloy Composition

Boron (B), % 0 to 0.0050
0
Carbon (C), % 0 to 0.18
0 to 0.080
Chromium (Cr), % 0 to 1.0
17 to 20
Copper (Cu), % 0 to 0.3
0 to 0.75
Iron (Fe), % 93.6 to 100
58.6 to 69.5
Manganese (Mn), % 0 to 1.7
0.5 to 2.5
Molybdenum (Mo), % 0 to 0.7
2.0 to 3.0
Nickel (Ni), % 0 to 1.5
11 to 14
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.080
0
Zirconium (Zr), % 0 to 0.15
0