EN 1.8874 Steel vs. EN 1.0108 Steel

Both EN 1.8874 steel and EN 1.0108 steel are iron alloys. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.8874 steel and the bottom bar is EN 1.0108 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
110
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
29
Fatigue Strength, MPa 340
150
Impact Strength: V-Notched Charpy, J 68
38
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 410
250
Tensile Strength: Ultimate (UTS), MPa 660
380
Tensile Strength: Yield (Proof), MPa 500
200

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
50
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 3.2
2.1
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.8
1.5
Embodied Energy, MJ/kg 24
19
Embodied Water, L/kg 52
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
94
Resilience: Unit (Modulus of Resilience), kJ/m3 670
110
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
13
Strength to Weight: Bending, points 21
15
Thermal Diffusivity, mm2/s 10
13
Thermal Shock Resistance, points 19
12

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.2
Boron (B), % 0 to 0.0050
0
Carbon (C), % 0 to 0.18
0 to 0.13
Chromium (Cr), % 0 to 1.0
0 to 0.3
Copper (Cu), % 0 to 0.3
0 to 0.3
Iron (Fe), % 93.6 to 100
97.5 to 99.98
Manganese (Mn), % 0 to 1.7
0 to 0.7
Molybdenum (Mo), % 0 to 0.7
0 to 0.080
Nickel (Ni), % 0 to 1.5
0 to 0.3
Niobium (Nb), % 0 to 0.050
0 to 0.010
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.6
0 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0 to 0.050
0 to 0.040
Vanadium (V), % 0 to 0.080
0 to 0.020
Zirconium (Zr), % 0 to 0.15
0