EN 1.8891 Steel vs. EN 1.4832 Stainless Steel

Both EN 1.8891 steel and EN 1.4832 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.8891 steel and the bottom bar is EN 1.4832 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
150
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
11
Fatigue Strength, MPa 330
140
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 610
510
Tensile Strength: Yield (Proof), MPa 480
260

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
950
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 46
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
19
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
3.6
Embodied Energy, MJ/kg 24
51
Embodied Water, L/kg 51
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
48
Resilience: Unit (Modulus of Resilience), kJ/m3 630
170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
18
Strength to Weight: Bending, points 20
18
Thermal Diffusivity, mm2/s 12
3.7
Thermal Shock Resistance, points 18
12

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0 to 0.2
0.15 to 0.35
Chromium (Cr), % 0 to 0.3
19 to 21
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 95.2 to 99
58.6 to 67.4
Manganese (Mn), % 1.0 to 1.7
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
0 to 0.5
Nickel (Ni), % 0 to 0.8
13 to 15
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.025
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.6
0.5 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.2
0