EN 1.8893 Steel vs. EN 1.0535 Steel

Both EN 1.8893 steel and EN 1.0535 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.8893 steel and the bottom bar is EN 1.0535 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 16
12
Fatigue Strength, MPa 470
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Shear Strength, MPa 510
420
Tensile Strength: Ultimate (UTS), MPa 830
690
Tensile Strength: Yield (Proof), MPa 720
340

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
48
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 23
19
Embodied Water, L/kg 51
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
69
Resilience: Unit (Modulus of Resilience), kJ/m3 1370
310
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 29
25
Strength to Weight: Bending, points 25
22
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 24
22

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0 to 0.2
0.52 to 0.6
Chromium (Cr), % 0 to 0.3
0 to 0.4
Copper (Cu), % 0 to 0.2
0
Iron (Fe), % 95.6 to 98
97.1 to 98.9
Manganese (Mn), % 1.4 to 1.7
0.6 to 0.9
Molybdenum (Mo), % 0.3 to 0.45
0 to 0.1
Nickel (Ni), % 0.3 to 0.7
0 to 0.4
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.045
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.12
0