EN 1.8932 Steel vs. Grade 14 Titanium

EN 1.8932 steel belongs to the iron alloys classification, while grade 14 titanium belongs to the titanium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.8932 steel and the bottom bar is grade 14 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 20
23
Fatigue Strength, MPa 250
220
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 73
41
Shear Strength, MPa 370
290
Tensile Strength: Ultimate (UTS), MPa 600
460
Tensile Strength: Yield (Proof), MPa 370
310

Thermal Properties

Latent Heat of Fusion, J/g 250
420
Maximum Temperature: Mechanical, °C 410
320
Melting Completion (Liquidus), °C 1460
1660
Melting Onset (Solidus), °C 1420
1610
Specific Heat Capacity, J/kg-K 470
540
Thermal Conductivity, W/m-K 40
21
Thermal Expansion, µm/m-K 13
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
3.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
6.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
37
Density, g/cm3 7.8
4.5
Embodied Carbon, kg CO2/kg material 1.7
32
Embodied Energy, MJ/kg 24
520
Embodied Water, L/kg 50
210

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
93
Resilience: Unit (Modulus of Resilience), kJ/m3 370
450
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
35
Strength to Weight: Axial, points 21
28
Strength to Weight: Bending, points 20
29
Thermal Diffusivity, mm2/s 11
8.5
Thermal Shock Resistance, points 17
35

Alloy Composition

Aluminum (Al), % 0 to 0.060
0
Carbon (C), % 0 to 0.2
0 to 0.080
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.2
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 95.5 to 98.9
0 to 0.3
Manganese (Mn), % 1.0 to 1.7
0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 1.0
0.4 to 0.6
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0 to 0.030
Oxygen (O), % 0
0 to 0.15
Phosphorus (P), % 0 to 0.025
0
Ruthenium (Ru), % 0
0.040 to 0.060
Silicon (Si), % 0.1 to 0.6
0
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
98.4 to 99.56
Vanadium (V), % 0 to 0.2
0
Residuals, % 0
0 to 0.4