MakeItFrom.com
Menu (ESC)

EN 2.4663 Nickel vs. CR009A Copper

EN 2.4663 nickel belongs to the nickel alloys classification, while CR009A copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 2.4663 nickel and the bottom bar is CR009A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
120
Elongation at Break, % 40
15
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 81
43
Tensile Strength: Ultimate (UTS), MPa 780
230
Tensile Strength: Yield (Proof), MPa 310
140

Thermal Properties

Latent Heat of Fusion, J/g 320
210
Maximum Temperature: Mechanical, °C 1010
200
Melting Completion (Liquidus), °C 1430
1090
Melting Onset (Solidus), °C 1380
1040
Specific Heat Capacity, J/kg-K 450
390
Thermal Conductivity, W/m-K 13
380
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
100
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
100

Otherwise Unclassified Properties

Base Metal Price, % relative 75
31
Density, g/cm3 8.6
9.0
Embodied Carbon, kg CO2/kg material 11
2.6
Embodied Energy, MJ/kg 140
41
Embodied Water, L/kg 350
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 250
31
Resilience: Unit (Modulus of Resilience), kJ/m3 230
83
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 23
18
Strength to Weight: Axial, points 25
7.1
Strength to Weight: Bending, points 22
9.3
Thermal Diffusivity, mm2/s 3.5
110
Thermal Shock Resistance, points 22
8.1

Alloy Composition

Aluminum (Al), % 0.7 to 1.4
0
Antimony (Sb), % 0
0 to 0.00040
Arsenic (As), % 0
0 to 0.00050
Bismuth (Bi), % 0
0 to 0.00020
Boron (B), % 0 to 0.0060
0
Cadmium (Cd), % 0
0 to 0.00010
Carbon (C), % 0.050 to 0.1
0
Chromium (Cr), % 20 to 23
0
Cobalt (Co), % 11 to 14
0
Copper (Cu), % 0 to 0.5
99.99 to 100
Iron (Fe), % 0 to 2.0
0 to 0.0010
Lead (Pb), % 0
0 to 0.00050
Manganese (Mn), % 0 to 0.2
0 to 0.00050
Molybdenum (Mo), % 8.5 to 10
0
Nickel (Ni), % 48 to 59.6
0 to 0.0010
Phosphorus (P), % 0 to 0.010
0 to 0.0030
Selenium (Se), % 0
0 to 0.00020
Silicon (Si), % 0 to 0.2
0
Silver (Ag), % 0
0 to 0.0025
Sulfur (S), % 0 to 0.010
0 to 0.0015
Tellurium (Te), % 0
0 to 0.00020
Tin (Sn), % 0
0 to 0.00020
Titanium (Ti), % 0.2 to 0.6
0
Zinc (Zn), % 0
0 to 0.00010