EN 2.4669 Nickel vs. 60Cr-40Ni Alloy
EN 2.4669 nickel belongs to the nickel alloys classification, while 60Cr-40Ni alloy belongs to the otherwise unclassified metals. They have 55% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is EN 2.4669 nickel and the bottom bar is 60Cr-40Ni alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
220 |
Poisson's Ratio | 0.29 | |
0.25 |
Shear Modulus, GPa | 73 | |
87 |
Tensile Strength: Ultimate (UTS), MPa | 1110 | |
870 |
Tensile Strength: Yield (Proof), MPa | 720 | |
660 |
Thermal Properties
Latent Heat of Fusion, J/g | 310 | |
370 |
Specific Heat Capacity, J/kg-K | 460 | |
490 |
Thermal Expansion, µm/m-K | 13 | |
16 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 60 | |
49 |
Density, g/cm3 | 8.4 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 10 | |
7.4 |
Embodied Energy, MJ/kg | 150 | |
110 |
Embodied Water, L/kg | 260 | |
380 |
Common Calculations
Resilience: Unit (Modulus of Resilience), kJ/m3 | 1380 | |
1000 |
Stiffness to Weight: Axial, points | 13 | |
16 |
Stiffness to Weight: Bending, points | 23 | |
26 |
Strength to Weight: Axial, points | 37 | |
31 |
Strength to Weight: Bending, points | 28 | |
26 |
Thermal Shock Resistance, points | 33 | |
18 |
Alloy Composition
Aluminum (Al), % | 0.4 to 1.0 | |
0 to 0.25 |
Carbon (C), % | 0 to 0.080 | |
0 to 0.1 |
Chromium (Cr), % | 14 to 17 | |
58 to 62 |
Cobalt (Co), % | 0 to 1.0 | |
0 |
Copper (Cu), % | 0 to 0.5 | |
0 |
Iron (Fe), % | 5.0 to 9.0 | |
0 to 1.0 |
Manganese (Mn), % | 0 to 1.0 | |
0 to 0.3 |
Nickel (Ni), % | 65.9 to 77.7 | |
34.5 to 42 |
Niobium (Nb), % | 0.7 to 1.2 | |
0 |
Nitrogen (N), % | 0 | |
0 to 0.3 |
Phosphorus (P), % | 0 to 0.020 | |
0 to 0.020 |
Silicon (Si), % | 0 to 0.5 | |
0 to 1.0 |
Sulfur (S), % | 0 to 0.015 | |
0 to 0.020 |
Titanium (Ti), % | 2.3 to 2.8 | |
0 to 0.5 |