EN 2.4851 Nickel vs. 5457 Aluminum
EN 2.4851 nickel belongs to the nickel alloys classification, while 5457 aluminum belongs to the aluminum alloys. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 2.4851 nickel and the bottom bar is 5457 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 32 to 55 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 68 |
| Elongation at Break, % | 34 | |
| 6.0 to 22 |
| Fatigue Strength, MPa | 170 | |
| 55 to 98 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 76 | |
| 26 |
| Shear Strength, MPa | 430 | |
| 85 to 130 |
| Tensile Strength: Ultimate (UTS), MPa | 650 | |
| 130 to 210 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 50 to 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 1200 | |
| 180 |
| Melting Completion (Liquidus), °C | 1360 | |
| 660 |
| Melting Onset (Solidus), °C | 1310 | |
| 630 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 900 |
| Thermal Conductivity, W/m-K | 11 | |
| 180 |
| Thermal Expansion, µm/m-K | 14 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.4 | |
| 46 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.6 | |
| 150 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 49 | |
| 9.5 |
| Density, g/cm3 | 8.2 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 8.4 |
| Embodied Energy, MJ/kg | 120 | |
| 160 |
| Embodied Water, L/kg | 280 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 12 to 23 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 | |
| 18 to 250 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 50 |
| Strength to Weight: Axial, points | 22 | |
| 13 to 21 |
| Strength to Weight: Bending, points | 20 | |
| 21 to 28 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 72 |
| Thermal Shock Resistance, points | 17 | |
| 5.7 to 9.0 |
Alloy Composition
| Aluminum (Al), % | 1.0 to 1.7 | |
| 97.8 to 99.05 |
| Boron (B), % | 0 to 0.0060 | |
| 0 |
| Carbon (C), % | 0.030 to 0.1 | |
| 0 |
| Chromium (Cr), % | 21 to 25 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.2 |
| Iron (Fe), % | 7.7 to 18 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 0 | |
| 0.8 to 1.2 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.15 to 0.45 |
| Nickel (Ni), % | 58 to 63 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.080 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0 to 0.050 |
| Zinc (Zn), % | 0 | |
| 0 to 0.050 |
| Residuals, % | 0 | |
| 0 to 0.1 |