EN 2.4878 Nickel vs. AISI 301LN Stainless Steel
EN 2.4878 nickel belongs to the nickel alloys classification, while AISI 301LN stainless steel belongs to the iron alloys. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 2.4878 nickel and the bottom bar is AISI 301LN stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 13 to 17 | |
| 23 to 51 |
| Fatigue Strength, MPa | 400 to 410 | |
| 270 to 520 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 78 | |
| 77 |
| Shear Strength, MPa | 750 to 760 | |
| 450 to 670 |
| Tensile Strength: Ultimate (UTS), MPa | 1210 to 1250 | |
| 630 to 1060 |
| Tensile Strength: Yield (Proof), MPa | 740 to 780 | |
| 270 to 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 1030 | |
| 890 |
| Melting Completion (Liquidus), °C | 1370 | |
| 1430 |
| Melting Onset (Solidus), °C | 1320 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 15 |
| Thermal Expansion, µm/m-K | 12 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 80 | |
| 13 |
| Density, g/cm3 | 8.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 2.7 |
| Embodied Energy, MJ/kg | 150 | |
| 39 |
| Embodied Water, L/kg | 370 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 180 | |
| 220 to 290 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1370 to 1540 | |
| 180 to 1520 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 41 to 42 | |
| 22 to 38 |
| Strength to Weight: Bending, points | 31 | |
| 21 to 30 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 4.0 |
| Thermal Shock Resistance, points | 37 to 39 | |
| 14 to 24 |
Alloy Composition
| Aluminum (Al), % | 1.2 to 1.6 | |
| 0 |
| Boron (B), % | 0.010 to 0.015 | |
| 0 |
| Carbon (C), % | 0.030 to 0.070 | |
| 0 to 0.030 |
| Chromium (Cr), % | 23 to 25 | |
| 16 to 18 |
| Cobalt (Co), % | 19 to 21 | |
| 0 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 |
| Iron (Fe), % | 0 to 1.0 | |
| 70.7 to 77.9 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 1.0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 43.6 to 52.2 | |
| 6.0 to 8.0 |
| Niobium (Nb), % | 0.7 to 1.2 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0.070 to 0.2 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.0070 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 0 to 0.050 | |
| 0 |
| Titanium (Ti), % | 2.8 to 3.2 | |
| 0 |
| Zirconium (Zr), % | 0.030 to 0.070 | |
| 0 |