EN 2.4878 Nickel vs. AWS ERNiMo-3
Both EN 2.4878 nickel and AWS ERNiMo-3 are nickel alloys. They have 57% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 2.4878 nickel and the bottom bar is AWS ERNiMo-3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 220 |
| Poisson's Ratio | 0.29 | |
| 0.3 |
| Shear Modulus, GPa | 78 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 1210 to 1250 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 320 |
| Melting Completion (Liquidus), °C | 1370 | |
| 1600 |
| Melting Onset (Solidus), °C | 1320 | |
| 1540 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 400 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 80 | |
| 70 |
| Density, g/cm3 | 8.3 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 15 |
| Embodied Energy, MJ/kg | 150 | |
| 190 |
| Embodied Water, L/kg | 370 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 22 |
| Strength to Weight: Axial, points | 41 to 42 | |
| 24 |
| Strength to Weight: Bending, points | 31 | |
| 21 |
| Thermal Shock Resistance, points | 37 to 39 | |
| 24 |
Alloy Composition
| Aluminum (Al), % | 1.2 to 1.6 | |
| 0 |
| Boron (B), % | 0.010 to 0.015 | |
| 0 |
| Carbon (C), % | 0.030 to 0.070 | |
| 0 to 0.12 |
| Chromium (Cr), % | 23 to 25 | |
| 4.0 to 6.0 |
| Cobalt (Co), % | 19 to 21 | |
| 0 to 2.5 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 1.0 | |
| 4.0 to 7.0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 1.0 to 2.0 | |
| 23 to 26 |
| Nickel (Ni), % | 43.6 to 52.2 | |
| 53.7 to 69 |
| Niobium (Nb), % | 0.7 to 1.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.0070 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 0 to 0.050 | |
| 0 |
| Titanium (Ti), % | 2.8 to 3.2 | |
| 0 |
| Tungsten (W), % | 0 | |
| 0 to 1.0 |
| Vanadium (V), % | 0 | |
| 0 to 0.6 |
| Zirconium (Zr), % | 0.030 to 0.070 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |