EN 2.4878 Nickel vs. Monel R-405
Both EN 2.4878 nickel and Monel R-405 are nickel alloys. They have 49% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 2.4878 nickel and the bottom bar is Monel R-405.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 160 |
| Elongation at Break, % | 13 to 17 | |
| 9.1 to 39 |
| Fatigue Strength, MPa | 400 to 410 | |
| 210 to 250 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 78 | |
| 62 |
| Shear Strength, MPa | 750 to 760 | |
| 350 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 1210 to 1250 | |
| 540 to 630 |
| Tensile Strength: Yield (Proof), MPa | 740 to 780 | |
| 190 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 1030 | |
| 900 |
| Melting Completion (Liquidus), °C | 1370 | |
| 1350 |
| Melting Onset (Solidus), °C | 1320 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 430 |
| Thermal Conductivity, W/m-K | 11 | |
| 23 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 80 | |
| 50 |
| Density, g/cm3 | 8.3 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 7.9 |
| Embodied Energy, MJ/kg | 150 | |
| 110 |
| Embodied Water, L/kg | 370 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 180 | |
| 49 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1370 to 1540 | |
| 120 to 370 |
| Stiffness to Weight: Axial, points | 13 | |
| 10 |
| Stiffness to Weight: Bending, points | 24 | |
| 21 |
| Strength to Weight: Axial, points | 41 to 42 | |
| 17 to 20 |
| Strength to Weight: Bending, points | 31 | |
| 17 to 18 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 5.9 |
| Thermal Shock Resistance, points | 37 to 39 | |
| 17 to 20 |
Alloy Composition
| Aluminum (Al), % | 1.2 to 1.6 | |
| 0 |
| Boron (B), % | 0.010 to 0.015 | |
| 0 |
| Carbon (C), % | 0.030 to 0.070 | |
| 0 to 0.3 |
| Chromium (Cr), % | 23 to 25 | |
| 0 |
| Cobalt (Co), % | 19 to 21 | |
| 0 |
| Copper (Cu), % | 0 to 0.2 | |
| 28 to 34 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 2.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 1.0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 43.6 to 52.2 | |
| 63 to 72 |
| Niobium (Nb), % | 0.7 to 1.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.0070 | |
| 0.025 to 0.060 |
| Tantalum (Ta), % | 0 to 0.050 | |
| 0 |
| Titanium (Ti), % | 2.8 to 3.2 | |
| 0 |
| Zirconium (Zr), % | 0.030 to 0.070 | |
| 0 |