EN 2.4878 Nickel vs. R05240 Alloy
EN 2.4878 nickel belongs to the nickel alloys classification, while R05240 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 2.4878 nickel and the bottom bar is R05240 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 150 |
| Elongation at Break, % | 13 to 17 | |
| 25 |
| Poisson's Ratio | 0.29 | |
| 0.36 |
| Shear Modulus, GPa | 78 | |
| 57 |
| Tensile Strength: Ultimate (UTS), MPa | 1210 to 1250 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 740 to 780 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 210 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 190 |
| Thermal Expansion, µm/m-K | 12 | |
| 6.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 14 |
| Embodied Water, L/kg | 370 | |
| 460 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 180 | |
| 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1370 to 1540 | |
| 90 |
| Stiffness to Weight: Axial, points | 13 | |
| 6.3 |
| Stiffness to Weight: Bending, points | 24 | |
| 13 |
| Strength to Weight: Axial, points | 41 to 42 | |
| 5.4 |
| Strength to Weight: Bending, points | 31 | |
| 6.8 |
| Thermal Shock Resistance, points | 37 to 39 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 1.2 to 1.6 | |
| 0 |
| Boron (B), % | 0.010 to 0.015 | |
| 0 |
| Carbon (C), % | 0.030 to 0.070 | |
| 0 to 0.010 |
| Chromium (Cr), % | 23 to 25 | |
| 0 |
| Cobalt (Co), % | 19 to 21 | |
| 0 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Molybdenum (Mo), % | 1.0 to 2.0 | |
| 0 to 0.020 |
| Nickel (Ni), % | 43.6 to 52.2 | |
| 0 to 0.010 |
| Niobium (Nb), % | 0.7 to 1.2 | |
| 35 to 42 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.0070 | |
| 0 |
| Tantalum (Ta), % | 0 to 0.050 | |
| 57.9 to 65 |
| Titanium (Ti), % | 2.8 to 3.2 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 0 to 0.050 |
| Zirconium (Zr), % | 0.030 to 0.070 | |
| 0 |