EN 2.4889 Nickel vs. C82000 Copper

EN 2.4889 nickel belongs to the nickel alloys classification, while C82000 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 2.4889 nickel and the bottom bar is C82000 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 39
8.0 to 20
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
45
Tensile Strength: Ultimate (UTS), MPa 720
350 to 690
Tensile Strength: Yield (Proof), MPa 270
140 to 520

Thermal Properties

Latent Heat of Fusion, J/g 350
220
Maximum Temperature: Mechanical, °C 1200
220
Melting Completion (Liquidus), °C 1350
1090
Melting Onset (Solidus), °C 1300
970
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 13
260
Thermal Expansion, µm/m-K 14
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
45
Electrical Conductivity: Equal Weight (Specific), % IACS 1.6
46

Otherwise Unclassified Properties

Base Metal Price, % relative 42
60
Density, g/cm3 8.0
8.9
Embodied Carbon, kg CO2/kg material 6.9
5.0
Embodied Energy, MJ/kg 98
77
Embodied Water, L/kg 250
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
51 to 55
Resilience: Unit (Modulus of Resilience), kJ/m3 180
80 to 1120
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 25
11 to 22
Strength to Weight: Bending, points 22
12 to 20
Thermal Diffusivity, mm2/s 3.4
76
Thermal Shock Resistance, points 19
12 to 24

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Beryllium (Be), % 0
0.45 to 0.8
Carbon (C), % 0.050 to 0.12
0
Cerium (Ce), % 0.030 to 0.090
0
Chromium (Cr), % 26 to 29
0 to 0.1
Cobalt (Co), % 0
2.2 to 2.7
Copper (Cu), % 0 to 0.3
95.2 to 97.4
Iron (Fe), % 21 to 25
0 to 0.1
Lead (Pb), % 0
0 to 0.020
Manganese (Mn), % 0 to 1.0
0
Nickel (Ni), % 45 to 50.4
0 to 0.2
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 2.5 to 3.0
0 to 0.15
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
0 to 0.1
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.5