MakeItFrom.com
Menu (ESC)

EN 2.4951 Nickel vs. S32803 Stainless Steel

EN 2.4951 nickel belongs to the nickel alloys classification, while S32803 stainless steel belongs to the iron alloys. They have a modest 26% of their average alloy composition in common, which, by itself, doesn't mean much. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 2.4951 nickel and the bottom bar is S32803 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
210
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 34
18
Fatigue Strength, MPa 200
350
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 76
81
Shear Strength, MPa 500
420
Tensile Strength: Ultimate (UTS), MPa 750
680
Tensile Strength: Yield (Proof), MPa 270
560

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Maximum Temperature: Mechanical, °C 1150
1100
Melting Completion (Liquidus), °C 1360
1450
Melting Onset (Solidus), °C 1310
1400
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.6
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.7
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 60
19
Density, g/cm3 8.5
7.7
Embodied Carbon, kg CO2/kg material 9.3
3.7
Embodied Energy, MJ/kg 130
53
Embodied Water, L/kg 280
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
120
Resilience: Unit (Modulus of Resilience), kJ/m3 190
760
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 25
25
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 3.1
4.4
Thermal Shock Resistance, points 23
22

Alloy Composition

Aluminum (Al), % 0 to 0.3
0
Carbon (C), % 0.080 to 0.15
0 to 0.015
Chromium (Cr), % 18 to 21
28 to 29
Cobalt (Co), % 0 to 5.0
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 5.0
62.9 to 67.1
Manganese (Mn), % 0 to 1.0
0 to 0.5
Molybdenum (Mo), % 0
1.8 to 2.5
Nickel (Ni), % 65.4 to 81.7
3.0 to 4.0
Niobium (Nb), % 0
0.15 to 0.5
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.020
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.55
Sulfur (S), % 0 to 0.015
0 to 0.0035
Titanium (Ti), % 0.2 to 0.6
0