EN 2.4952 Nickel vs. SAE-AISI 1010 Steel
EN 2.4952 nickel belongs to the nickel alloys classification, while SAE-AISI 1010 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 2.4952 nickel and the bottom bar is SAE-AISI 1010 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 17 | |
| 22 to 31 |
| Fatigue Strength, MPa | 370 | |
| 150 to 230 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 14 | |
| 46 to 56 |
| Shear Modulus, GPa | 74 | |
| 73 |
| Shear Strength, MPa | 700 | |
| 230 to 250 |
| Tensile Strength: Ultimate (UTS), MPa | 1150 | |
| 350 to 400 |
| Tensile Strength: Yield (Proof), MPa | 670 | |
| 190 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 400 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1470 |
| Melting Onset (Solidus), °C | 1300 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 12 | |
| 47 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.4 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.5 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 55 | |
| 1.8 |
| Density, g/cm3 | 8.3 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 9.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 140 | |
| 18 |
| Embodied Water, L/kg | 290 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 82 to 93 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1180 | |
| 100 to 290 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 38 | |
| 12 to 14 |
| Strength to Weight: Bending, points | 29 | |
| 14 to 15 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 13 |
| Thermal Shock Resistance, points | 33 | |
| 11 to 13 |
Alloy Composition
| Aluminum (Al), % | 1.0 to 1.8 | |
| 0 |
| Boron (B), % | 0 to 0.0080 | |
| 0 |
| Carbon (C), % | 0.040 to 0.1 | |
| 0.080 to 0.13 |
| Chromium (Cr), % | 18 to 21 | |
| 0 |
| Cobalt (Co), % | 0 to 1.0 | |
| 0 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 |
| Iron (Fe), % | 0 to 1.5 | |
| 99.18 to 99.62 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.3 to 0.6 |
| Nickel (Ni), % | 65 to 79.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.050 |
| Titanium (Ti), % | 1.8 to 2.7 | |
| 0 |