EN AC-42000 Aluminum vs. Monel K-500
EN AC-42000 aluminum belongs to the aluminum alloys classification, while Monel K-500 belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN AC-42000 aluminum and the bottom bar is Monel K-500.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 160 |
| Elongation at Break, % | 1.1 to 2.4 | |
| 25 to 36 |
| Fatigue Strength, MPa | 67 to 76 | |
| 260 to 560 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 61 |
| Tensile Strength: Ultimate (UTS), MPa | 170 to 270 | |
| 640 to 1100 |
| Tensile Strength: Yield (Proof), MPa | 95 to 230 | |
| 310 to 880 |
Thermal Properties
| Latent Heat of Fusion, J/g | 500 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 900 |
| Melting Completion (Liquidus), °C | 610 | |
| 1350 |
| Melting Onset (Solidus), °C | 600 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 440 |
| Thermal Conductivity, W/m-K | 160 | |
| 18 |
| Thermal Expansion, µm/m-K | 22 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 38 | |
| 3.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 3.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 50 |
| Density, g/cm3 | 2.6 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 8.1 |
| Embodied Energy, MJ/kg | 150 | |
| 120 |
| Embodied Water, L/kg | 1110 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.8 to 5.7 | |
| 180 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 64 to 370 | |
| 300 to 2420 |
| Stiffness to Weight: Axial, points | 15 | |
| 10 |
| Stiffness to Weight: Bending, points | 53 | |
| 21 |
| Strength to Weight: Axial, points | 18 to 28 | |
| 21 to 35 |
| Strength to Weight: Bending, points | 26 to 35 | |
| 19 to 27 |
| Thermal Diffusivity, mm2/s | 66 | |
| 4.8 |
| Thermal Shock Resistance, points | 7.9 to 12 | |
| 21 to 36 |
Alloy Composition
| Aluminum (Al), % | 89.9 to 93.3 | |
| 2.3 to 3.2 |
| Carbon (C), % | 0 | |
| 0 to 0.18 |
| Copper (Cu), % | 0 to 0.2 | |
| 27 to 33 |
| Iron (Fe), % | 0 to 0.55 | |
| 0 to 2.0 |
| Lead (Pb), % | 0 to 0.15 | |
| 0 |
| Magnesium (Mg), % | 0.2 to 0.65 | |
| 0 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 to 1.5 |
| Nickel (Ni), % | 0 to 0.15 | |
| 63 to 70.4 |
| Silicon (Si), % | 6.5 to 7.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 0 to 0.050 | |
| 0 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0.35 to 0.85 |
| Zinc (Zn), % | 0 to 0.15 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |