EN AC-42100 Aluminum vs. K93600 Alloy
EN AC-42100 aluminum belongs to the aluminum alloys classification, while K93600 alloy belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN AC-42100 aluminum and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 140 |
| Elongation at Break, % | 3.4 to 9.0 | |
| 5.0 to 35 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 290 | |
| 480 to 810 |
| Tensile Strength: Yield (Proof), MPa | 210 to 230 | |
| 280 to 750 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 170 | |
| 440 |
| Melting Onset (Solidus), °C | 600 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 910 | |
| 520 |
| Thermal Conductivity, W/m-K | 150 | |
| 13 |
| Thermal Expansion, µm/m-K | 22 | |
| 7.3 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 41 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 2.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.6 | |
| 8.1 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.1 to 23 | |
| 21 to 280 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 to 370 | |
| 280 to 2050 |
| Stiffness to Weight: Axial, points | 15 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 53 | |
| 21 |
| Strength to Weight: Axial, points | 30 to 31 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 37 to 38 | |
| 17 to 24 |
| Thermal Diffusivity, mm2/s | 66 | |
| 3.1 |
| Thermal Shock Resistance, points | 13 | |
| 34 to 57 |