EN AC-43300 Aluminum vs. Grade 19 Titanium
EN AC-43300 aluminum belongs to the aluminum alloys classification, while grade 19 titanium belongs to the titanium alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN AC-43300 aluminum and the bottom bar is grade 19 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 120 |
| Elongation at Break, % | 3.4 to 6.7 | |
| 5.6 to 17 |
| Fatigue Strength, MPa | 76 to 77 | |
| 550 to 620 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 27 | |
| 47 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 290 | |
| 890 to 1300 |
| Tensile Strength: Yield (Proof), MPa | 210 to 230 | |
| 870 to 1170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 540 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 370 |
| Melting Completion (Liquidus), °C | 600 | |
| 1660 |
| Melting Onset (Solidus), °C | 590 | |
| 1600 |
| Specific Heat Capacity, J/kg-K | 910 | |
| 520 |
| Thermal Conductivity, W/m-K | 140 | |
| 6.2 |
| Thermal Expansion, µm/m-K | 22 | |
| 9.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 45 |
| Density, g/cm3 | 2.5 | |
| 5.0 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 47 |
| Embodied Energy, MJ/kg | 150 | |
| 760 |
| Embodied Water, L/kg | 1080 | |
| 230 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.1 to 17 | |
| 70 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 to 370 | |
| 3040 to 5530 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 54 | |
| 33 |
| Strength to Weight: Axial, points | 31 to 32 | |
| 49 to 72 |
| Strength to Weight: Bending, points | 37 to 38 | |
| 41 to 53 |
| Thermal Diffusivity, mm2/s | 59 | |
| 2.4 |
| Thermal Shock Resistance, points | 13 to 14 | |
| 57 to 83 |
Alloy Composition
| Aluminum (Al), % | 88.9 to 90.8 | |
| 3.0 to 4.0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 5.5 to 6.5 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.020 |
| Iron (Fe), % | 0 to 0.19 | |
| 0 to 0.3 |
| Magnesium (Mg), % | 0.25 to 0.45 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.12 |
| Silicon (Si), % | 9.0 to 10 | |
| 0 |
| Titanium (Ti), % | 0 to 0.15 | |
| 71.1 to 77 |
| Vanadium (V), % | 0 | |
| 7.5 to 8.5 |
| Zinc (Zn), % | 0 to 0.070 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |