EN AC-43400 Aluminum vs. C19200 Copper

EN AC-43400 aluminum belongs to the aluminum alloys classification, while C19200 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN AC-43400 aluminum and the bottom bar is C19200 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 72
120
Elongation at Break, % 1.1
2.0 to 35
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 27
44
Tensile Strength: Ultimate (UTS), MPa 270
280 to 530
Tensile Strength: Yield (Proof), MPa 160
98 to 510

Thermal Properties

Latent Heat of Fusion, J/g 540
210
Maximum Temperature: Mechanical, °C 170
200
Melting Completion (Liquidus), °C 600
1080
Melting Onset (Solidus), °C 590
1080
Specific Heat Capacity, J/kg-K 900
390
Thermal Conductivity, W/m-K 140
240
Thermal Expansion, µm/m-K 22
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 32
58 to 74
Electrical Conductivity: Equal Weight (Specific), % IACS 110
58 to 75

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
30
Density, g/cm3 2.6
8.9
Embodied Carbon, kg CO2/kg material 7.8
2.6
Embodied Energy, MJ/kg 150
41
Embodied Water, L/kg 1070
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.6
10 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 180
42 to 1120
Stiffness to Weight: Axial, points 15
7.2
Stiffness to Weight: Bending, points 54
18
Strength to Weight: Axial, points 29
8.8 to 17
Strength to Weight: Bending, points 36
11 to 16
Thermal Diffusivity, mm2/s 59
69
Thermal Shock Resistance, points 12
10 to 19

Alloy Composition

Aluminum (Al), % 86 to 90.8
0
Copper (Cu), % 0 to 0.1
98.5 to 99.19
Iron (Fe), % 0 to 1.0
0.8 to 1.2
Lead (Pb), % 0 to 0.15
0 to 0.030
Magnesium (Mg), % 0.2 to 0.5
0
Manganese (Mn), % 0 to 0.55
0
Nickel (Ni), % 0 to 0.15
0
Phosphorus (P), % 0
0.010 to 0.040
Silicon (Si), % 9.0 to 11
0
Tin (Sn), % 0 to 0.050
0
Titanium (Ti), % 0 to 0.2
0
Zinc (Zn), % 0 to 0.15
0 to 0.2
Residuals, % 0
0 to 0.2