EN AC-44200 Aluminum vs. EN AC-51500 Aluminum
Both EN AC-44200 aluminum and EN AC-51500 aluminum are aluminum alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a moderately high 90% of their average alloy composition in common.
For each property being compared, the top bar is EN AC-44200 aluminum and the bottom bar is EN AC-51500 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 60 | |
| 80 |
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 68 |
| Elongation at Break, % | 6.2 | |
| 5.6 |
| Fatigue Strength, MPa | 63 | |
| 120 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 280 |
| Tensile Strength: Yield (Proof), MPa | 86 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 570 | |
| 430 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 170 |
| Melting Completion (Liquidus), °C | 590 | |
| 630 |
| Melting Onset (Solidus), °C | 580 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 910 | |
| 910 |
| Thermal Conductivity, W/m-K | 130 | |
| 120 |
| Thermal Expansion, µm/m-K | 21 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 88 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.5 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 9.0 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 1050 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.1 | |
| 13 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 51 | |
| 190 |
| Stiffness to Weight: Axial, points | 16 | |
| 14 |
| Stiffness to Weight: Bending, points | 55 | |
| 52 |
| Strength to Weight: Axial, points | 20 | |
| 29 |
| Strength to Weight: Bending, points | 28 | |
| 36 |
| Thermal Diffusivity, mm2/s | 59 | |
| 49 |
| Thermal Shock Resistance, points | 8.4 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 85.2 to 89.5 | |
| 89.8 to 93.1 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.050 |
| Iron (Fe), % | 0 to 0.55 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 0 | |
| 4.7 to 6.0 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0.4 to 0.8 |
| Silicon (Si), % | 10.5 to 13.5 | |
| 1.8 to 2.6 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.070 |
| Residuals, % | 0 | |
| 0 to 0.15 |