EN AC-44500 Aluminum vs. 444.0 Aluminum
Both EN AC-44500 aluminum and 444.0 aluminum are aluminum alloys. They have a moderately high 95% of their average alloy composition in common.
For each property being compared, the top bar is EN AC-44500 aluminum and the bottom bar is 444.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 68 | |
| 50 |
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 71 |
| Elongation at Break, % | 1.1 | |
| 25 |
| Fatigue Strength, MPa | 110 | |
| 51 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 190 |
| Tensile Strength: Yield (Proof), MPa | 160 | |
| 83 |
Thermal Properties
| Latent Heat of Fusion, J/g | 570 | |
| 500 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 170 |
| Melting Completion (Liquidus), °C | 590 | |
| 610 |
| Melting Onset (Solidus), °C | 580 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 130 | |
| 160 |
| Thermal Expansion, µm/m-K | 21 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 33 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.5 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 7.9 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 1050 | |
| 1110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.6 | |
| 39 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 49 |
| Stiffness to Weight: Axial, points | 16 | |
| 15 |
| Stiffness to Weight: Bending, points | 55 | |
| 53 |
| Strength to Weight: Axial, points | 29 | |
| 20 |
| Strength to Weight: Bending, points | 36 | |
| 28 |
| Thermal Diffusivity, mm2/s | 57 | |
| 67 |
| Thermal Shock Resistance, points | 13 | |
| 8.8 |
Alloy Composition
| Aluminum (Al), % | 83.7 to 89.5 | |
| 90.5 to 93.5 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.6 |
| Magnesium (Mg), % | 0 to 0.4 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 0.55 | |
| 0 to 0.35 |
| Silicon (Si), % | 10.5 to 13.5 | |
| 6.5 to 7.5 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 0.3 | |
| 0 to 0.35 |
| Residuals, % | 0 | |
| 0 to 0.15 |