EN AC-46200 Aluminum vs. 2219 Aluminum
Both EN AC-46200 aluminum and 2219 aluminum are aluminum alloys. They have 90% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN AC-46200 aluminum and the bottom bar is 2219 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 73 | |
| 72 |
| Elongation at Break, % | 1.1 | |
| 2.2 to 20 |
| Fatigue Strength, MPa | 87 | |
| 90 to 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 210 | |
| 180 to 480 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 88 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 510 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 230 |
| Melting Completion (Liquidus), °C | 620 | |
| 640 |
| Melting Onset (Solidus), °C | 540 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 870 |
| Thermal Conductivity, W/m-K | 110 | |
| 110 to 170 |
| Thermal Expansion, µm/m-K | 22 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 28 to 44 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 88 | |
| 81 to 130 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 11 |
| Density, g/cm3 | 2.8 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 8.2 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 1060 | |
| 1130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.0 | |
| 9.6 to 60 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 | |
| 54 to 1060 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 44 |
| Strength to Weight: Axial, points | 21 | |
| 16 to 43 |
| Strength to Weight: Bending, points | 28 | |
| 23 to 44 |
| Thermal Diffusivity, mm2/s | 44 | |
| 42 to 63 |
| Thermal Shock Resistance, points | 9.5 | |
| 8.2 to 22 |
Alloy Composition
| Aluminum (Al), % | 82.6 to 90.3 | |
| 91.5 to 93.8 |
| Copper (Cu), % | 2.0 to 3.5 | |
| 5.8 to 6.8 |
| Iron (Fe), % | 0 to 0.8 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 to 0.25 | |
| 0 |
| Magnesium (Mg), % | 0.050 to 0.55 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0.15 to 0.65 | |
| 0.2 to 0.4 |
| Nickel (Ni), % | 0 to 0.35 | |
| 0 |
| Silicon (Si), % | 7.5 to 9.5 | |
| 0 to 0.2 |
| Tin (Sn), % | 0 to 0.15 | |
| 0 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0.020 to 0.1 |
| Vanadium (V), % | 0 | |
| 0.050 to 0.15 |
| Zinc (Zn), % | 0 to 1.2 | |
| 0 to 0.1 |
| Zirconium (Zr), % | 0 | |
| 0.1 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |