EN AC-46400 Aluminum vs. Grade 705C Zirconium
EN AC-46400 aluminum belongs to the aluminum alloys classification, while grade 705C zirconium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN AC-46400 aluminum and the bottom bar is grade 705C zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 77 to 120 | |
| 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 98 |
| Elongation at Break, % | 1.1 to 1.7 | |
| 13 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 27 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 170 to 310 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 110 to 270 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 520 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 270 |
| Thermal Conductivity, W/m-K | 130 | |
| 18 |
| Thermal Expansion, µm/m-K | 22 | |
| 5.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 6.7 |
| Embodied Water, L/kg | 1070 | |
| 450 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 1.7 to 4.9 | |
| 66 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 82 to 500 | |
| 790 |
| Stiffness to Weight: Axial, points | 15 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 52 | |
| 23 |
| Strength to Weight: Axial, points | 18 to 32 | |
| 22 |
| Strength to Weight: Bending, points | 26 to 38 | |
| 22 |
| Thermal Diffusivity, mm2/s | 55 | |
| 9.9 |
| Thermal Shock Resistance, points | 7.8 to 14 | |
| 69 |
Alloy Composition
| Aluminum (Al), % | 85.4 to 90.5 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0.8 to 1.3 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 0 to 0.8 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Magnesium (Mg), % | 0.25 to 0.65 | |
| 0 |
| Manganese (Mn), % | 0.15 to 0.55 | |
| 0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 2.0 to 3.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 8.3 to 9.7 | |
| 0 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0 to 0.8 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 91.9 to 98 |
| Residuals, % | 0 to 0.25 | |
| 0 |