EN AC-48100 Aluminum vs. EN 1.4107 Stainless Steel
EN AC-48100 aluminum belongs to the aluminum alloys classification, while EN 1.4107 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN AC-48100 aluminum and the bottom bar is EN 1.4107 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 76 | |
| 190 |
| Elongation at Break, % | 1.1 | |
| 18 to 21 |
| Fatigue Strength, MPa | 120 to 130 | |
| 260 to 350 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 29 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 240 to 330 | |
| 620 to 700 |
| Tensile Strength: Yield (Proof), MPa | 190 to 300 | |
| 400 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 640 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 740 |
| Melting Completion (Liquidus), °C | 580 | |
| 1450 |
| Melting Onset (Solidus), °C | 470 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 480 |
| Thermal Conductivity, W/m-K | 130 | |
| 27 |
| Thermal Expansion, µm/m-K | 20 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 87 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 7.5 |
| Density, g/cm3 | 2.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 7.3 | |
| 2.1 |
| Embodied Energy, MJ/kg | 130 | |
| 30 |
| Embodied Water, L/kg | 940 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.3 to 3.6 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 580 | |
| 420 to 840 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 25 |
| Strength to Weight: Axial, points | 24 to 33 | |
| 22 to 25 |
| Strength to Weight: Bending, points | 31 to 38 | |
| 21 to 22 |
| Thermal Diffusivity, mm2/s | 55 | |
| 7.2 |
| Thermal Shock Resistance, points | 11 to 16 | |
| 22 to 25 |
Alloy Composition
| Aluminum (Al), % | 72.1 to 79.8 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 11.5 to 12.5 |
| Copper (Cu), % | 4.0 to 5.0 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 1.3 | |
| 83.8 to 87.2 |
| Magnesium (Mg), % | 0.25 to 0.65 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0.8 to 1.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 16 to 18 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Tin (Sn), % | 0 to 0.15 | |
| 0 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0 to 0.080 |
| Zinc (Zn), % | 0 to 1.5 | |
| 0 |
| Residuals, % | 0 to 0.25 | |
| 0 |