EN AC-71100 Aluminum vs. 6016 Aluminum
Both EN AC-71100 aluminum and 6016 aluminum are aluminum alloys. They have 83% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN AC-71100 aluminum and the bottom bar is 6016 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 110 | |
| 55 to 80 |
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 69 |
| Elongation at Break, % | 1.1 | |
| 11 to 27 |
| Fatigue Strength, MPa | 150 | |
| 68 to 89 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 260 | |
| 200 to 280 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 110 to 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 490 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 160 |
| Melting Completion (Liquidus), °C | 580 | |
| 660 |
| Melting Onset (Solidus), °C | 520 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 860 | |
| 900 |
| Thermal Expansion, µm/m-K | 22 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 32 | |
| 48 to 54 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 97 | |
| 160 to 180 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.9 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 8.2 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 1010 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.8 | |
| 29 to 47 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 | |
| 82 to 340 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 47 | |
| 51 |
| Strength to Weight: Axial, points | 25 | |
| 21 to 29 |
| Strength to Weight: Bending, points | 31 | |
| 29 to 35 |
| Thermal Shock Resistance, points | 12 | |
| 9.1 to 12 |
Alloy Composition
| Aluminum (Al), % | 78.7 to 83.3 | |
| 96.4 to 98.8 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0.2 to 0.5 | |
| 0.25 to 0.6 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 to 0.2 |
| Silicon (Si), % | 7.5 to 9.5 | |
| 1.0 to 1.5 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 to 0.15 |
| Zinc (Zn), % | 9.0 to 10.5 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |