CC140C Copper vs. SAE-AISI 4028 Steel

CC140C copper belongs to the copper alloys classification, while SAE-AISI 4028 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is CC140C copper and the bottom bar is SAE-AISI 4028 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110
150 to 190
Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 11
14 to 23
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 44
73
Tensile Strength: Ultimate (UTS), MPa 340
490 to 630
Tensile Strength: Yield (Proof), MPa 230
260 to 520

Thermal Properties

Latent Heat of Fusion, J/g 210
250
Maximum Temperature: Mechanical, °C 200
400
Melting Completion (Liquidus), °C 1100
1460
Melting Onset (Solidus), °C 1040
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 310
49
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 77
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 78
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.1
Density, g/cm3 8.9
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.5
Embodied Energy, MJ/kg 41
19
Embodied Water, L/kg 310
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 34
81 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 220
180 to 720
Stiffness to Weight: Axial, points 7.3
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 10
17 to 22
Strength to Weight: Bending, points 12
18 to 21
Thermal Diffusivity, mm2/s 89
13
Thermal Shock Resistance, points 12
16 to 20

Alloy Composition

Carbon (C), % 0
0.25 to 0.3
Chromium (Cr), % 0.4 to 1.2
0
Copper (Cu), % 98.8 to 99.6
0
Iron (Fe), % 0
98.1 to 98.7
Manganese (Mn), % 0
0.7 to 0.9
Molybdenum (Mo), % 0
0.2 to 0.3
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0.15 to 0.35
Sulfur (S), % 0
0.035 to 0.050