CC212E Bronze vs. Grade 18 Titanium
CC212E bronze belongs to the copper alloys classification, while grade 18 titanium belongs to the titanium alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is CC212E bronze and the bottom bar is grade 18 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 110 |
| Elongation at Break, % | 20 | |
| 11 to 17 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 47 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 690 to 980 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 540 to 810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 330 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1640 |
| Melting Onset (Solidus), °C | 1020 | |
| 1590 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 550 |
| Thermal Expansion, µm/m-K | 18 | |
| 9.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.0 | |
| 1.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 2.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 41 |
| Embodied Energy, MJ/kg | 55 | |
| 670 |
| Embodied Water, L/kg | 370 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 87 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 390 | |
| 1380 to 3110 |
| Stiffness to Weight: Axial, points | 8.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 35 |
| Strength to Weight: Axial, points | 24 | |
| 43 to 61 |
| Strength to Weight: Bending, points | 21 | |
| 39 to 49 |
| Thermal Shock Resistance, points | 22 | |
| 47 to 67 |
Alloy Composition
| Aluminum (Al), % | 7.0 to 9.0 | |
| 2.5 to 3.5 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 68 to 77 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 2.0 to 4.0 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 8.0 to 15 | |
| 0 |
| Nickel (Ni), % | 1.5 to 4.5 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.15 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 0 to 0.5 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 92.5 to 95.5 |
| Vanadium (V), % | 0 | |
| 2.0 to 3.0 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |