CC330G Bronze vs. EN 1.1147 Steel
CC330G bronze belongs to the copper alloys classification, while EN 1.1147 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is CC330G bronze and the bottom bar is EN 1.1147 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 110 | |
| 110 to 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 20 | |
| 12 to 17 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 530 | |
| 390 to 470 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 280 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 400 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1460 |
| Melting Onset (Solidus), °C | 1000 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 470 |
| Thermal Conductivity, W/m-K | 62 | |
| 51 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 15 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 1.8 |
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 1.4 |
| Embodied Energy, MJ/kg | 52 | |
| 18 |
| Embodied Water, L/kg | 390 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 82 | |
| 40 to 73 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 210 to 370 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 18 | |
| 14 to 17 |
| Strength to Weight: Bending, points | 17 | |
| 15 to 17 |
| Thermal Diffusivity, mm2/s | 17 | |
| 14 |
| Thermal Shock Resistance, points | 19 | |
| 12 to 15 |
Alloy Composition
| Aluminum (Al), % | 8.0 to 10.5 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.15 to 0.19 |
| Copper (Cu), % | 87 to 92 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 1.2 | |
| 98.3 to 99.25 |
| Lead (Pb), % | 0 to 0.3 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.6 to 0.9 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Tin (Sn), % | 0 to 0.3 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |