CC330G Bronze vs. C97400 Nickel Silver
Both CC330G bronze and C97400 nickel silver are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 61% of their average alloy composition in common.
For each property being compared, the top bar is CC330G bronze and the bottom bar is C97400 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 110 | |
| 70 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 20 | |
| 20 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Shear Modulus, GPa | 42 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 530 | |
| 260 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 180 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1100 |
| Melting Onset (Solidus), °C | 1000 | |
| 1070 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 380 |
| Thermal Conductivity, W/m-K | 62 | |
| 27 |
| Thermal Expansion, µm/m-K | 18 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 6.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 15 | |
| 6.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 33 |
| Density, g/cm3 | 8.4 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 4.1 |
| Embodied Energy, MJ/kg | 52 | |
| 64 |
| Embodied Water, L/kg | 390 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 82 | |
| 43 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 59 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 18 | |
| 8.5 |
| Strength to Weight: Bending, points | 17 | |
| 11 |
| Thermal Diffusivity, mm2/s | 17 | |
| 8.3 |
| Thermal Shock Resistance, points | 19 | |
| 8.8 |
Alloy Composition
| Aluminum (Al), % | 8.0 to 10.5 | |
| 0 |
| Copper (Cu), % | 87 to 92 | |
| 58 to 61 |
| Iron (Fe), % | 0 to 1.2 | |
| 0 to 1.5 |
| Lead (Pb), % | 0 to 0.3 | |
| 4.5 to 5.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 1.0 | |
| 15.5 to 17 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 |
| Tin (Sn), % | 0 to 0.3 | |
| 2.5 to 3.5 |
| Zinc (Zn), % | 0 to 0.5 | |
| 10 to 19.5 |
| Residuals, % | 0 | |
| 0 to 1.0 |