CC331G Bronze vs. R05240 Alloy
CC331G bronze belongs to the copper alloys classification, while R05240 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is CC331G bronze and the bottom bar is R05240 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 150 |
| Elongation at Break, % | 20 | |
| 25 |
| Poisson's Ratio | 0.34 | |
| 0.36 |
| Shear Modulus, GPa | 43 | |
| 57 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 240 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 210 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 190 |
| Thermal Expansion, µm/m-K | 18 | |
| 6.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 14 |
| Embodied Water, L/kg | 390 | |
| 460 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 97 | |
| 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 | |
| 90 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 6.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 13 |
| Strength to Weight: Axial, points | 21 | |
| 5.4 |
| Strength to Weight: Bending, points | 19 | |
| 6.8 |
| Thermal Shock Resistance, points | 22 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 8.5 to 10.5 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Copper (Cu), % | 83 to 86.5 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 1.5 to 3.5 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.020 |
| Nickel (Ni), % | 0 to 1.5 | |
| 0 to 0.010 |
| Niobium (Nb), % | 0 | |
| 35 to 42 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.0050 |
| Tantalum (Ta), % | 0 | |
| 57.9 to 65 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 0 to 0.050 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |