CC332G Bronze vs. SAE-AISI H11 Steel

CC332G bronze belongs to the copper alloys classification, while SAE-AISI H11 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is CC332G bronze and the bottom bar is SAE-AISI H11 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
74
Tensile Strength: Ultimate (UTS), MPa 620
690 to 1840

Thermal Properties

Latent Heat of Fusion, J/g 230
270
Melting Completion (Liquidus), °C 1060
1460
Melting Onset (Solidus), °C 1010
1410
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 45
42
Thermal Expansion, µm/m-K 18
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 12
9.5

Otherwise Unclassified Properties

Base Metal Price, % relative 29
5.5
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 3.4
3.0
Embodied Energy, MJ/kg 55
43
Embodied Water, L/kg 390
75

Common Calculations

Stiffness to Weight: Axial, points 7.7
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 21
25 to 66
Strength to Weight: Bending, points 19
22 to 43
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 21
22 to 58

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Carbon (C), % 0
0.33 to 0.43
Chromium (Cr), % 0
4.8 to 5.5
Copper (Cu), % 80 to 86
0 to 0.25
Iron (Fe), % 1.0 to 3.0
89.6 to 92.5
Lead (Pb), % 0 to 0.1
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 2.0
0.2 to 0.5
Molybdenum (Mo), % 0
1.1 to 1.6
Nickel (Ni), % 1.5 to 4.0
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.2
0.8 to 1.2
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.2
0
Vanadium (V), % 0
0.3 to 0.6
Zinc (Zn), % 0 to 0.5
0