CC334G Bronze vs. SAE-AISI S2 Steel

CC334G bronze belongs to the copper alloys classification, while SAE-AISI S2 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is CC334G bronze and the bottom bar is SAE-AISI S2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 45
72
Tensile Strength: Ultimate (UTS), MPa 810
670 to 1940

Thermal Properties

Latent Heat of Fusion, J/g 240
260
Melting Completion (Liquidus), °C 1080
1450
Melting Onset (Solidus), °C 1020
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 41
44
Thermal Expansion, µm/m-K 18
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 29
2.6
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 3.6
2.1
Embodied Energy, MJ/kg 59
30
Embodied Water, L/kg 390
49

Common Calculations

Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 28
24 to 69
Strength to Weight: Bending, points 24
22 to 44
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 28
23 to 68

Alloy Composition

Aluminum (Al), % 10 to 12
0
Carbon (C), % 0
0.4 to 0.55
Copper (Cu), % 72 to 84.5
0 to 0.25
Iron (Fe), % 3.0 to 7.0
96 to 98.1
Lead (Pb), % 0 to 0.050
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 2.5
0.3 to 0.5
Molybdenum (Mo), % 0
0.3 to 0.6
Nickel (Ni), % 4.0 to 7.5
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.1
0.9 to 1.2
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.2
0
Vanadium (V), % 0
0 to 0.5
Zinc (Zn), % 0 to 0.5
0