CC382H Copper-nickel vs. C72700 Copper-nickel
Both CC382H copper-nickel and C72700 copper-nickel are copper alloys. They have 75% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is CC382H copper-nickel and the bottom bar is C72700 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 120 |
| Elongation at Break, % | 20 | |
| 4.0 to 36 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 53 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 490 | |
| 460 to 1070 |
| Tensile Strength: Yield (Proof), MPa | 290 | |
| 580 to 1060 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 260 | |
| 200 |
| Melting Completion (Liquidus), °C | 1180 | |
| 1100 |
| Melting Onset (Solidus), °C | 1120 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 380 |
| Thermal Conductivity, W/m-K | 30 | |
| 54 |
| Thermal Expansion, µm/m-K | 15 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.5 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.6 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 41 | |
| 36 |
| Density, g/cm3 | 8.9 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 5.2 | |
| 4.0 |
| Embodied Energy, MJ/kg | 76 | |
| 62 |
| Embodied Water, L/kg | 290 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 85 | |
| 20 to 380 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 | |
| 1420 to 4770 |
| Stiffness to Weight: Axial, points | 8.8 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 20 | |
| 19 |
| Strength to Weight: Axial, points | 15 | |
| 14 to 34 |
| Strength to Weight: Bending, points | 16 | |
| 15 to 26 |
| Thermal Diffusivity, mm2/s | 8.2 | |
| 16 |
| Thermal Shock Resistance, points | 16 | |
| 16 to 38 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.0020 | |
| 0 |
| Boron (B), % | 0 to 0.010 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 1.5 to 2.0 | |
| 0 |
| Copper (Cu), % | 62.8 to 68.4 | |
| 82.1 to 86 |
| Iron (Fe), % | 0.5 to 1.0 | |
| 0 to 0.5 |
| Lead (Pb), % | 0 to 0.0050 | |
| 0 to 0.020 |
| Magnesium (Mg), % | 0 to 0.010 | |
| 0 to 0.15 |
| Manganese (Mn), % | 0.5 to 1.0 | |
| 0.050 to 0.3 |
| Nickel (Ni), % | 29 to 32 | |
| 8.5 to 9.5 |
| Niobium (Nb), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Selenium (Se), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Tellurium (Te), % | 0 to 0.0050 | |
| 0 |
| Tin (Sn), % | 0 | |
| 5.5 to 6.5 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.5 |
| Zirconium (Zr), % | 0 to 0.15 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.3 |