CC484K Bronze vs. ASTM A182 Grade F12 Class 1

CC484K bronze belongs to the copper alloys classification, while ASTM A182 grade F12 class 1 belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is CC484K bronze and the bottom bar is ASTM A182 grade F12 class 1.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 100
150
Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 11
23
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 41
73
Tensile Strength: Ultimate (UTS), MPa 330
470
Tensile Strength: Yield (Proof), MPa 200
250

Thermal Properties

Latent Heat of Fusion, J/g 190
250
Maximum Temperature: Mechanical, °C 170
430
Melting Completion (Liquidus), °C 1000
1470
Melting Onset (Solidus), °C 870
1420
Specific Heat Capacity, J/kg-K 370
470
Thermal Conductivity, W/m-K 70
45
Thermal Expansion, µm/m-K 18
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.1
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 9.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 37
2.8
Density, g/cm3 8.7
7.9
Embodied Carbon, kg CO2/kg material 3.9
1.6
Embodied Energy, MJ/kg 64
21
Embodied Water, L/kg 400
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 32
91
Resilience: Unit (Modulus of Resilience), kJ/m3 180
160
Stiffness to Weight: Axial, points 6.9
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 10
17
Strength to Weight: Bending, points 12
17
Thermal Diffusivity, mm2/s 22
12
Thermal Shock Resistance, points 12
14

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Antimony (Sb), % 0 to 0.1
0
Carbon (C), % 0
0.050 to 0.15
Chromium (Cr), % 0
0.8 to 1.3
Copper (Cu), % 84.5 to 87.5
0
Iron (Fe), % 0 to 0.2
96.8 to 98.4
Lead (Pb), % 0 to 0.3
0
Manganese (Mn), % 0 to 0.2
0.3 to 0.6
Molybdenum (Mo), % 0
0.44 to 0.65
Nickel (Ni), % 1.5 to 2.5
0
Phosphorus (P), % 0.050 to 0.4
0 to 0.045
Silicon (Si), % 0 to 0.010
0 to 0.5
Sulfur (S), % 0 to 0.050
0 to 0.045
Tin (Sn), % 11 to 13
0
Zinc (Zn), % 0 to 0.4
0