CC484K Bronze vs. EN 1.4162 Stainless Steel

CC484K bronze belongs to the copper alloys classification, while EN 1.4162 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CC484K bronze and the bottom bar is EN 1.4162 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 100
250
Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 11
32
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 41
78
Tensile Strength: Ultimate (UTS), MPa 330
780
Tensile Strength: Yield (Proof), MPa 200
520

Thermal Properties

Latent Heat of Fusion, J/g 190
290
Maximum Temperature: Mechanical, °C 170
1000
Melting Completion (Liquidus), °C 1000
1420
Melting Onset (Solidus), °C 870
1370
Specific Heat Capacity, J/kg-K 370
480
Thermal Conductivity, W/m-K 70
15
Thermal Expansion, µm/m-K 18
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 37
12
Density, g/cm3 8.7
7.7
Embodied Carbon, kg CO2/kg material 3.9
2.6
Embodied Energy, MJ/kg 64
38
Embodied Water, L/kg 400
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 32
220
Resilience: Unit (Modulus of Resilience), kJ/m3 180
690
Stiffness to Weight: Axial, points 6.9
14
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 10
28
Strength to Weight: Bending, points 12
25
Thermal Diffusivity, mm2/s 22
4.0
Thermal Shock Resistance, points 12
21

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Antimony (Sb), % 0 to 0.1
0
Carbon (C), % 0
0 to 0.040
Chromium (Cr), % 0
21 to 22
Copper (Cu), % 84.5 to 87.5
0.1 to 0.8
Iron (Fe), % 0 to 0.2
67.2 to 73.3
Lead (Pb), % 0 to 0.3
0
Manganese (Mn), % 0 to 0.2
4.0 to 6.0
Molybdenum (Mo), % 0
0.1 to 0.8
Nickel (Ni), % 1.5 to 2.5
1.4 to 1.9
Nitrogen (N), % 0
0.2 to 0.25
Phosphorus (P), % 0.050 to 0.4
0 to 0.040
Silicon (Si), % 0 to 0.010
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.015
Tin (Sn), % 11 to 13
0
Zinc (Zn), % 0 to 0.4
0