CC493K Bronze vs. Nickel 600

CC493K bronze belongs to the copper alloys classification, while nickel 600 belongs to the nickel alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CC493K bronze and the bottom bar is nickel 600.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
190
Elongation at Break, % 14
3.4 to 35
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 39
75
Tensile Strength: Ultimate (UTS), MPa 270
650 to 990
Tensile Strength: Yield (Proof), MPa 140
270 to 760

Thermal Properties

Latent Heat of Fusion, J/g 180
310
Maximum Temperature: Mechanical, °C 160
1100
Melting Completion (Liquidus), °C 960
1410
Melting Onset (Solidus), °C 880
1350
Specific Heat Capacity, J/kg-K 360
460
Thermal Conductivity, W/m-K 61
14
Thermal Expansion, µm/m-K 19
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 12
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 32
55
Density, g/cm3 8.9
8.5
Embodied Carbon, kg CO2/kg material 3.3
9.0
Embodied Energy, MJ/kg 53
130
Embodied Water, L/kg 370
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 33
31 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 89
190 to 1490
Stiffness to Weight: Axial, points 6.5
13
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 8.6
21 to 32
Strength to Weight: Bending, points 11
20 to 26
Thermal Diffusivity, mm2/s 19
3.6
Thermal Shock Resistance, points 10
19 to 29

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Antimony (Sb), % 0 to 0.3
0
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
14 to 17
Copper (Cu), % 79 to 86
0 to 0.5
Iron (Fe), % 0 to 0.2
6.0 to 10
Lead (Pb), % 5.0 to 8.0
0
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0 to 2.0
72 to 80
Phosphorus (P), % 0 to 0.1
0
Silicon (Si), % 0 to 0.010
0 to 0.5
Sulfur (S), % 0 to 0.1
0 to 0.015
Tin (Sn), % 5.2 to 8.0
0
Zinc (Zn), % 2.0 to 5.0
0