CC493K Bronze vs. SAE-AISI 4340 Steel
CC493K bronze belongs to the copper alloys classification, while SAE-AISI 4340 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is CC493K bronze and the bottom bar is SAE-AISI 4340 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 74 | |
| 210 to 360 |
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 14 | |
| 12 to 22 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 39 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 690 to 1280 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 470 to 1150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 430 |
| Melting Completion (Liquidus), °C | 960 | |
| 1460 |
| Melting Onset (Solidus), °C | 880 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 360 | |
| 470 |
| Thermal Conductivity, W/m-K | 61 | |
| 44 |
| Thermal Expansion, µm/m-K | 19 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 7.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 3.5 |
| Density, g/cm3 | 8.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 1.7 |
| Embodied Energy, MJ/kg | 53 | |
| 22 |
| Embodied Water, L/kg | 370 | |
| 53 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 33 | |
| 79 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 89 | |
| 590 to 3490 |
| Stiffness to Weight: Axial, points | 6.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 8.6 | |
| 24 to 45 |
| Strength to Weight: Bending, points | 11 | |
| 22 to 33 |
| Thermal Diffusivity, mm2/s | 19 | |
| 12 |
| Thermal Shock Resistance, points | 10 | |
| 20 to 38 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.3 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.38 to 0.43 |
| Chromium (Cr), % | 0 | |
| 0.7 to 0.9 |
| Copper (Cu), % | 79 to 86 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 95.1 to 96.3 |
| Lead (Pb), % | 5.0 to 8.0 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.6 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0.2 to 0.3 |
| Nickel (Ni), % | 0 to 2.0 | |
| 1.7 to 2.0 |
| Phosphorus (P), % | 0 to 0.1 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.010 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.1 | |
| 0 to 0.040 |
| Tin (Sn), % | 5.2 to 8.0 | |
| 0 |
| Zinc (Zn), % | 2.0 to 5.0 | |
| 0 |