CC495K Bronze vs. N06045 Nickel

CC495K bronze belongs to the copper alloys classification, while N06045 nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is CC495K bronze and the bottom bar is N06045 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
200
Elongation at Break, % 7.0
37
Poisson's Ratio 0.35
0.28
Shear Modulus, GPa 37
77
Tensile Strength: Ultimate (UTS), MPa 240
690
Tensile Strength: Yield (Proof), MPa 120
270

Thermal Properties

Latent Heat of Fusion, J/g 180
350
Maximum Temperature: Mechanical, °C 140
1010
Melting Completion (Liquidus), °C 930
1350
Melting Onset (Solidus), °C 820
1300
Specific Heat Capacity, J/kg-K 350
480
Thermal Expansion, µm/m-K 19
13

Otherwise Unclassified Properties

Base Metal Price, % relative 33
42
Density, g/cm3 9.0
8.0
Embodied Carbon, kg CO2/kg material 3.6
6.9
Embodied Energy, MJ/kg 58
98
Embodied Water, L/kg 400
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 14
200
Resilience: Unit (Modulus of Resilience), kJ/m3 68
180
Stiffness to Weight: Axial, points 6.2
14
Stiffness to Weight: Bending, points 17
24
Strength to Weight: Axial, points 7.3
24
Strength to Weight: Bending, points 9.4
22
Thermal Shock Resistance, points 8.8
18

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Antimony (Sb), % 0 to 0.5
0
Carbon (C), % 0
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.090
Chromium (Cr), % 0
26 to 29
Copper (Cu), % 76 to 82
0 to 0.3
Iron (Fe), % 0 to 0.25
21 to 25
Lead (Pb), % 8.0 to 11
0
Manganese (Mn), % 0 to 0.2
0 to 1.0
Nickel (Ni), % 0 to 2.0
45 to 50.4
Phosphorus (P), % 0 to 0.1
0 to 0.020
Silicon (Si), % 0 to 0.010
2.5 to 3.0
Sulfur (S), % 0 to 0.1
0 to 0.010
Tin (Sn), % 9.0 to 11
0
Zinc (Zn), % 0 to 2.0
0