CC499K Bronze vs. SAE-AISI 1010 Steel
CC499K bronze belongs to the copper alloys classification, while SAE-AISI 1010 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is CC499K bronze and the bottom bar is SAE-AISI 1010 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 73 | |
| 100 to 110 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 13 | |
| 22 to 31 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 41 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 260 | |
| 350 to 400 |
| Tensile Strength: Yield (Proof), MPa | 120 | |
| 190 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 400 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1470 |
| Melting Onset (Solidus), °C | 920 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 370 | |
| 470 |
| Thermal Conductivity, W/m-K | 73 | |
| 47 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 1.8 |
| Density, g/cm3 | 8.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 51 | |
| 18 |
| Embodied Water, L/kg | 350 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 | |
| 82 to 93 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 65 | |
| 100 to 290 |
| Stiffness to Weight: Axial, points | 6.9 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 8.1 | |
| 12 to 14 |
| Strength to Weight: Bending, points | 10 | |
| 14 to 15 |
| Thermal Diffusivity, mm2/s | 22 | |
| 13 |
| Thermal Shock Resistance, points | 9.2 | |
| 11 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.1 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.020 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.020 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.080 to 0.13 |
| Chromium (Cr), % | 0 to 0.020 | |
| 0 |
| Copper (Cu), % | 84 to 88 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 99.18 to 99.62 |
| Lead (Pb), % | 0 to 3.0 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.6 |
| Nickel (Ni), % | 0 to 0.6 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.050 |
| Tin (Sn), % | 4.0 to 6.0 | |
| 0 |
| Zinc (Zn), % | 4.0 to 6.0 | |
| 0 |