CC750S Brass vs. SAE-AISI 81B45 Steel

CC750S brass belongs to the copper alloys classification, while SAE-AISI 81B45 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is CC750S brass and the bottom bar is SAE-AISI 81B45 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 54
160 to 200
Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 13
12 to 24
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 40
73
Tensile Strength: Ultimate (UTS), MPa 200
540 to 670
Tensile Strength: Yield (Proof), MPa 80
350 to 560

Thermal Properties

Latent Heat of Fusion, J/g 170
250
Maximum Temperature: Mechanical, °C 130
410
Melting Completion (Liquidus), °C 860
1460
Melting Onset (Solidus), °C 810
1420
Specific Heat Capacity, J/kg-K 380
470
Thermal Conductivity, W/m-K 110
40
Thermal Expansion, µm/m-K 20
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 26
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.3
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.5
Embodied Energy, MJ/kg 46
20
Embodied Water, L/kg 330
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
77 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 30
320 to 840
Stiffness to Weight: Axial, points 7.1
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 6.8
19 to 24
Strength to Weight: Bending, points 9.3
19 to 22
Thermal Diffusivity, mm2/s 35
11
Thermal Shock Resistance, points 6.7
17 to 21

Alloy Composition

Aluminum (Al), % 0 to 0.1
0
Boron (B), % 0
0.00050 to 0.0030
Carbon (C), % 0
0.43 to 0.48
Chromium (Cr), % 0
0.35 to 0.55
Copper (Cu), % 62 to 67
0
Iron (Fe), % 0 to 0.8
97 to 98
Lead (Pb), % 1.0 to 3.0
0
Manganese (Mn), % 0 to 0.2
0.75 to 1.0
Molybdenum (Mo), % 0
0.080 to 0.15
Nickel (Ni), % 0 to 1.0
0.2 to 0.4
Phosphorus (P), % 0 to 0.050
0 to 0.035
Silicon (Si), % 0 to 0.050
0.15 to 0.35
Sulfur (S), % 0
0 to 0.040
Tin (Sn), % 0 to 1.5
0
Zinc (Zn), % 26.3 to 36
0