CC751S Brass vs. CC140C Copper
Both CC751S brass and CC140C copper are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 64% of their average alloy composition in common.
For each property being compared, the top bar is CC751S brass and the bottom bar is CC140C copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 130 | |
| 110 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 5.6 | |
| 11 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 450 | |
| 340 |
| Tensile Strength: Yield (Proof), MPa | 320 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 200 |
| Melting Completion (Liquidus), °C | 850 | |
| 1100 |
| Melting Onset (Solidus), °C | 810 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 110 | |
| 310 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 77 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 28 | |
| 78 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 31 |
| Density, g/cm3 | 8.1 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.6 |
| Embodied Energy, MJ/kg | 46 | |
| 41 |
| Embodied Water, L/kg | 330 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 23 | |
| 34 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 480 | |
| 220 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 15 | |
| 10 |
| Strength to Weight: Bending, points | 16 | |
| 12 |
| Thermal Diffusivity, mm2/s | 35 | |
| 89 |
| Thermal Shock Resistance, points | 15 | |
| 12 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.1 | |
| 0 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.4 to 1.2 |
| Copper (Cu), % | 62.7 to 66 | |
| 98.8 to 99.6 |
| Iron (Fe), % | 0.25 to 0.5 | |
| 0 |
| Lead (Pb), % | 0.8 to 2.2 | |
| 0 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 |
| Nickel (Ni), % | 0 to 0.8 | |
| 0 |
| Silicon (Si), % | 0.65 to 1.1 | |
| 0 |
| Tin (Sn), % | 0 to 0.8 | |
| 0 |
| Zinc (Zn), % | 27.9 to 35.6 | |
| 0 |