CC755S Brass vs. EN 1.3963 Alloy
CC755S brass belongs to the copper alloys classification, while EN 1.3963 alloy belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is CC755S brass and the bottom bar is EN 1.3963 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 9.5 | |
| 29 |
| Poisson's Ratio | 0.31 | |
| 0.3 |
| Shear Modulus, GPa | 40 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 390 | |
| 440 |
| Tensile Strength: Yield (Proof), MPa | 250 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 270 |
| Melting Completion (Liquidus), °C | 820 | |
| 1430 |
| Melting Onset (Solidus), °C | 780 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 460 |
| Thermal Expansion, µm/m-K | 21 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 25 |
| Density, g/cm3 | 8.1 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 4.8 |
| Embodied Energy, MJ/kg | 46 | |
| 66 |
| Embodied Water, L/kg | 330 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 33 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 | |
| 260 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 14 | |
| 15 |
| Strength to Weight: Bending, points | 15 | |
| 16 |
| Thermal Shock Resistance, points | 13 | |
| 110 |
Alloy Composition
| Aluminum (Al), % | 0.4 to 0.7 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 0 to 0.25 |
| Copper (Cu), % | 59.5 to 61 | |
| 0 |
| Iron (Fe), % | 0.050 to 0.2 | |
| 60.5 to 64.9 |
| Lead (Pb), % | 1.2 to 1.7 | |
| 0 |
| Manganese (Mn), % | 0 to 0.050 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 35 to 37 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.050 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0.1 to 0.2 |
| Tin (Sn), % | 0 to 0.3 | |
| 0 |
| Zinc (Zn), % | 35.8 to 38.9 | |
| 0 |