CC760S Brass vs. C36200 Brass

Both CC760S brass and C36200 brass are copper alloys. They have 76% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CC760S brass and the bottom bar is C36200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
100
Elongation at Break, % 22
20 to 53
Poisson's Ratio 0.33
0.31
Shear Modulus, GPa 42
39
Tensile Strength: Ultimate (UTS), MPa 180
340 to 420
Tensile Strength: Yield (Proof), MPa 80
130 to 360

Thermal Properties

Latent Heat of Fusion, J/g 190
170
Maximum Temperature: Mechanical, °C 170
120
Melting Completion (Liquidus), °C 1000
900
Melting Onset (Solidus), °C 940
890
Specific Heat Capacity, J/kg-K 390
380
Thermal Conductivity, W/m-K 150
120
Thermal Expansion, µm/m-K 19
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 38
26
Electrical Conductivity: Equal Weight (Specific), % IACS 40
28

Otherwise Unclassified Properties

Base Metal Price, % relative 28
23
Density, g/cm3 8.6
8.2
Embodied Carbon, kg CO2/kg material 2.6
2.6
Embodied Energy, MJ/kg 43
45
Embodied Water, L/kg 320
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 33
74 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 29
89 to 630
Stiffness to Weight: Axial, points 7.2
6.9
Stiffness to Weight: Bending, points 19
19
Strength to Weight: Axial, points 5.8
11 to 14
Strength to Weight: Bending, points 8.2
13 to 15
Thermal Diffusivity, mm2/s 45
37
Thermal Shock Resistance, points 6.2
11 to 14

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Arsenic (As), % 0.050 to 0.15
0
Copper (Cu), % 83 to 88
60 to 63
Iron (Fe), % 0 to 0.15
0 to 0.15
Lead (Pb), % 0 to 0.5
3.5 to 4.5
Manganese (Mn), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.1
0
Silicon (Si), % 0 to 0.020
0
Tin (Sn), % 0 to 0.3
0
Zinc (Zn), % 10.7 to 17
32.4 to 36.5