CR003A Copper vs. ASTM A182 Grade F911

CR003A copper belongs to the copper alloys classification, while ASTM A182 grade F911 belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CR003A copper and the bottom bar is ASTM A182 grade F911.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 15
20
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
76
Tensile Strength: Ultimate (UTS), MPa 230
690
Tensile Strength: Yield (Proof), MPa 140
500

Thermal Properties

Latent Heat of Fusion, J/g 210
270
Maximum Temperature: Mechanical, °C 200
600
Melting Completion (Liquidus), °C 1090
1480
Melting Onset (Solidus), °C 1040
1440
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 380
26
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
9.2
Electrical Conductivity: Equal Weight (Specific), % IACS 100
10

Otherwise Unclassified Properties

Base Metal Price, % relative 31
9.5
Density, g/cm3 9.0
7.9
Embodied Carbon, kg CO2/kg material 2.6
2.8
Embodied Energy, MJ/kg 41
40
Embodied Water, L/kg 310
90

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
130
Resilience: Unit (Modulus of Resilience), kJ/m3 83
650
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 7.1
24
Strength to Weight: Bending, points 9.3
22
Thermal Diffusivity, mm2/s 110
6.9
Thermal Shock Resistance, points 8.1
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Boron (B), % 0
0.00030 to 0.0060
Carbon (C), % 0
0.090 to 0.13
Chromium (Cr), % 0
8.5 to 9.5
Copper (Cu), % 99.954 to 100
0
Iron (Fe), % 0 to 0.0010
86.2 to 88.9
Lead (Pb), % 0 to 0.00050
0
Manganese (Mn), % 0
0.3 to 0.6
Molybdenum (Mo), % 0
0.9 to 1.1
Nickel (Ni), % 0
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.040 to 0.090
Oxygen (O), % 0 to 0.040
0
Phosphorus (P), % 0
0 to 0.020
Selenium (Se), % 0 to 0.00020
0
Silicon (Si), % 0
0.1 to 0.5
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0 to 0.010
Tellurium (Te), % 0 to 0.00020
0
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
0.9 to 1.1
Vanadium (V), % 0
0.18 to 0.25
Zirconium (Zr), % 0
0 to 0.010