CR003A Copper vs. R31539 Cobalt

CR003A copper belongs to the copper alloys classification, while R31539 cobalt belongs to the cobalt alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CR003A copper and the bottom bar is R31539 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
220
Elongation at Break, % 15
13 to 22
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
86
Tensile Strength: Ultimate (UTS), MPa 230
1000 to 1340
Tensile Strength: Yield (Proof), MPa 140
590 to 940

Thermal Properties

Latent Heat of Fusion, J/g 210
320
Melting Completion (Liquidus), °C 1090
1360
Melting Onset (Solidus), °C 1040
1290
Specific Heat Capacity, J/kg-K 390
450
Thermal Conductivity, W/m-K 380
13
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 100
2.1

Otherwise Unclassified Properties

Density, g/cm3 9.0
8.4
Embodied Carbon, kg CO2/kg material 2.6
8.2
Embodied Energy, MJ/kg 41
110
Embodied Water, L/kg 310
530

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
140 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 83
780 to 2000
Stiffness to Weight: Axial, points 7.2
15
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 7.1
33 to 44
Strength to Weight: Bending, points 9.3
27 to 32
Thermal Diffusivity, mm2/s 110
3.5
Thermal Shock Resistance, points 8.1
24 to 32

Alloy Composition

Aluminum (Al), % 0
0.3 to 1.0
Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Carbon (C), % 0
0 to 0.14
Chromium (Cr), % 0
26 to 30
Cobalt (Co), % 0
57.7 to 68.7
Copper (Cu), % 99.954 to 100
0
Iron (Fe), % 0 to 0.0010
0 to 0.75
Lanthanum (La), % 0
0.030 to 0.2
Lead (Pb), % 0 to 0.00050
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
5.0 to 7.0
Nickel (Ni), % 0
0 to 1.0
Nitrogen (N), % 0
0 to 0.25
Oxygen (O), % 0 to 0.040
0
Selenium (Se), % 0 to 0.00020
0
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0
Tellurium (Te), % 0 to 0.00020
0