CR003A Copper vs. CR006A Copper

Both CR003A copper and CR006A copper are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. Their average alloy composition is basically identical. There are 26 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is CR003A copper and the bottom bar is CR006A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 15
15
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 43
43
Tensile Strength: Ultimate (UTS), MPa 230
230
Tensile Strength: Yield (Proof), MPa 140
140

Thermal Properties

Latent Heat of Fusion, J/g 210
210
Maximum Temperature: Mechanical, °C 200
200
Melting Completion (Liquidus), °C 1090
1090
Melting Onset (Solidus), °C 1040
1040
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 380
380
Thermal Expansion, µm/m-K 17
17

Otherwise Unclassified Properties

Base Metal Price, % relative 31
31
Density, g/cm3 9.0
9.0
Embodied Carbon, kg CO2/kg material 2.6
2.6
Embodied Energy, MJ/kg 41
41
Embodied Water, L/kg 310
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
31
Resilience: Unit (Modulus of Resilience), kJ/m3 83
83
Stiffness to Weight: Axial, points 7.2
7.2
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 7.1
7.1
Strength to Weight: Bending, points 9.3
9.3
Thermal Diffusivity, mm2/s 110
110
Thermal Shock Resistance, points 8.1
8.1

Alloy Composition

Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Copper (Cu), % 99.954 to 100
99.9 to 100
Iron (Fe), % 0 to 0.0010
0
Lead (Pb), % 0 to 0.00050
0
Oxygen (O), % 0 to 0.040
0 to 0.1
Selenium (Se), % 0 to 0.00020
0
Silver (Ag), % 0 to 0.0025
0 to 0.015
Sulfur (S), % 0 to 0.0015
0
Tellurium (Te), % 0 to 0.00020
0